After mixing resin and slow hardener, you have 30 minutes to get it out of the cup and approximately 4 hours of open working at 70°F. Mix with appropriate MAS resins in a 2 parts resin to 1 part hardener ratio. Recommended for large surface coatings and laminations.
Storage Life: A minimum of 12 months in a sealed container at ambient temperatures.
- Blush Free - Recoat within 24 hours at 70° without washing/sanding the surface - save 60% labor.
- Good ultraviolet stability.
- Smooth finishes.
- Excellent barrier coating.
- Cures in high humidity.
- Blendable with fast or medium hardener for customized working and curing times.
| Watch Instructional Video: MAS Epoxy Resins & Hardeners |
|Click DOWNLOAD and then click OPEN to view the video clip. Videos may take up to 10 minutes to download depending on internet connection speed. |
| DOWNLOAD MAS Epoxy Resins & Hardeners .wmv file (12.5MB) |
|SPECIFICATIONS: ||CURE SCHEDULE: |
|Color (Gardner) ||3 ||Temperature ||Resin/Medium |
|Mix Ratio 2:1 Resin to Hardener || ||Fahrenheit ||Pot Life ||Thin Film Set ||Full Cure |
|Viscosity @ 77° F ||200 cps ||95° ||11.5 min ||2.5 hrs ||2.5 days |
|Specific Gravity @ 77° F ||0.998 ||86° ||17.25 min ||3.75 hrs ||3.75 days |
|Flash Point (closed cup) ||234° F ||77° ||23 min ||5 hrs ||5 days |
|Mixed Viscosity w/ MAS Resin @ 77° F ||500 - 600 cps ||68° ||34.5 min ||7.5 hrs ||7.5 days days |
|Peak Exotherm (100mg mix @ 77° F) ||250° F ||59° ||46 min ||10 hrs ||10 days |
'MAS Epoxies are the most advanced, high performance and user-friendly epoxy formulas in the world. We support all our products with knowledgeable, easy to reach staff, and provide a 100% money-back guarantee. Contact Mas Epoxies at 1-888-627-3769'
This product ships in 1 business day.
Add to Cart and enter your Postal Code to determine the shipping charges and estimated delivery date.
Most products and orders leave our warehouse in 1 business day. However, select items may take more processing time. Alaska and Hawaii orders please add 1 additional warehouse processing day.